Atron Nylon 6
| Atron 601 IM HS BK - Impact Modified, Heat Stabilized Nylon 6 for Injection Molding | |||
| Property | Nominal Value | Method | |
| English Units | SI Units | (ASTM) | |
| Properties measured dry as molded | |||
| General | |||
| Color | Black | ||
| Total Ash @ Typical Value | .40 % | .40 % | ASTM D789 |
| Moisture @ Typical Value | .25 % max. | .25 % max. | ASTM D789 |
| Specific Gravity | 1. 10 | 1.10 | ASTM D792 |
| Melt Point | 415 °F | 213 °C | ATR Method |
| Ti02 | .3 % max. | .3 % max. | |
| Physical | |||
| Tensile Strength | 8,500 psi | 59 MPa | ASTM D638 |
| Flexural Modulus | 328,000 | 2,262 MPa | ASTM D790 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Izod Impact, notched | 2.8 ft-lb/in | 149 J/m | ASTM D256 |
| Linear Mold Shrinkage | 0.01 in/in | 0.01 cm/cm | ASTM D955 |
| Heat Deflection Temp. @ 66 psi | 285 °F | 141 °C | ASTM D648 |
| Heat Deflection Temp. @ 264 psi | 126 °F | 52 °F | ASTM D648 |
| Hardness @ Rockwell R | 114 | 114 | ASTM D795 |
| Flammability | HB | HB | UL 94 |
| Date | 05/10/04 | ||
| Rev. | 5 | ||
| The information provided above is based on laboratory testing using the test methods indicated and is believed to represent nominal results of those tests. Because conditions under which this material may be processed, tested or used cannot be anticipated, no warranty is given, either expressed or implied, as to teh accuracy or reproducibility of this information or for the fitness of this material for any particular use. This Material is sold with the express understanding that purchasers, processors or other users of this material have sole responsibility, through performance of their own testing, to determine the suitability of this material for any particular use. | |||